XRD Analysis of Li4Ti5O12 with Post Heat Treatment for Lithium-ion Capacitor (LIC) Applications
DOI:
https://doi.org/10.32734/jotp.v4i1.8154Keywords:
Li4Ti5O12 Anode, Heat Treatment, Lithium Ion Capacitor, Sol GelAbstract
Characterization of XRD-analysis on Li4Ti5O12 with post heat treatment for applications Lithium-ion Capacitor (LIC) has been conducted. The powder method was used in the analysis, whereas the samples were prepared using the sol-gel method. The anode material Li4Ti5O12 precursor was sintered at 850°C for 4 hours and followed by heat-treatment at 600oC for 3 hours. Characterization of structural (XRD analysis) was applied to determine the formation of Li4Ti5O12 phase. The results of the characterization were formed Lithium titanate (Li4Ti5O12) and rutile phase (TiO2) with crystallite size on LTO I of 82.52 nm and LTO II of 92.07 nm. Overall, post heat treatment of anode Li4Ti5O12 succeeded in improving the quality and electrochemical performance for Lithium-ion Capacitor (LIC) application.
Downloads
Published
Issue
Section
Copyright (c) 2022 Journal of Technomaterial Physics
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.
The Authors submitting a manuscript do so on the understanding that if accepted for publication, copyright of the article shall be assigned to Jurnal Abdimas TALENTA as well as TALENTA Publisher Universitas Sumatera Utara as the publisher of the journal.
Copyright encompasses exclusive rights to reproduce and deliver the article in all forms and media. The reproduction of any part of this journal, its storage in databases and its transmission by any form or media, will be allowed only with written permission from Jurnal Abdimas TALENTA.
The Copyright Transfer Form can be downloaded here.
The copyright form should be signed originally and sent to the Editorial Office in the form of original mail or scanned document.